Temadur 20

Tikkurila Industry 9L
ОПИС A two component, semi-matt polyurethane paint containing anti-corrosive pigments, hardener aliphatic isocyanate.
КАРАКТЕРИСТИКИ НА ПРОИЗВООДОТ Recommended as a primer for polyurethane systems or as a semi-matt topcoat for epoxy systems exposed to weathering and/or chemical stress. Due to anti-corrosion pigments can also be used as a single coat system for steel, zinc and aluminium surfaces.
Перпорачана употреба Recommended for painting of transport and haulage equipment, storage tank exteriors, steel framework and other steel structures, machinery and equipment.

Features Excellent weathering and abrasion resistance. The product has MED (Marine Equipment Directive) certificate no
VTT-C-11167-15-14 and is thus accepted for painting surfaces inside the ships.
Colour Cards RAL, NCS, SSG, BS, MONICOLOR NOVA and SYMPHONY colour cards. TEMASPEED tinting.
Gloss groups Semi-matt

Recommended film thicknesses

Theoretical coverage




40 µm

 70 µm

14.2 m2/l

100 µm

175 µm

5.7 m2/l

Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Разредувач 1048 and 1067
Mixing ratio Base 5 parts by volume 114-s.
Hardener 1 part by volume 008 7590
Метод на примена By airless or conventional spray or by brush.
Pot-life (+23°C) 4 hours
Drying times

DFT 50 µm

+ 5 ºC

+ 10 ºC

+ 23 ºC

+ 35 ºC

Dust dry, after

45 min

30 min

15 min

10 min

Touch dry, after

8 h

6 h

4 h

2 h

Recoatable, after

No limitations.

Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Содржина на цврсти материи 57 ± 2 volume % (ISO 3233)
70 ± 2 weight %
Густина 1.3 ± 0.1 kg / l (mixed)
Шифра на производот 114-series
MED Certificate VTT C 11167 15 14 Temadur20 50

Услови за примена All surfaces must be dry. The temperature of the ambient air, surface or paint should not fall below + 5 ºC during application or drying. Relative humidity should not exceed 80 %. The surface temperature of the steel should remain at least 3 ºC above the dew point.
Припрема Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.

Zinc surfaces: Sweep blast clean with mineral abrasives, e.g. quartz sand, to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with PANSSARIPESU detergent.

Hot dip galvanized surfaces are recommended to be painted with a misty coat (paint thinned 25 - 30 %) before the actual priming.

Aluminium surfaces: Sweep blast clean with none-metallic abrasives to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with MAALIPESU detergent.

Stainless steel: Roughen the surface by grinding or sweep blasting using mineral abrasives.

Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
Priming Temacoat GPL-S Primer, Temacoat GPL-S MIO, Temacoat RM 40, Temacoat SPA, Temabond and Fontecoat EP 50.
Finishing Temadur and Temathane.
Премачкување By airless or conventional spray or by brush. Depending on the temperature of the components (base, hardener, thinner) and the required viscosity the paint can be thinned 0 - 20 %. Airless spray nozzle tip 0.011" - 0.015" and nozzle pressure 120 - 160 bar. Spray angle shall be chosen according to the shape of the object.
At brush application the paint should be thinned according to the circumstances.
Mixing of components First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use mechanical mixer for mixing.
Чистење на алатот Thinner 1048, 1067 or 1061.
EU VOC 2004/42/EC ограничена вредност The Volatile Organic Compounds amount is 420 g/litre of paint mixture.
VOC content of the paint mixture (thinned 20 % by volume) is 490 g/l.
Only for industrial use.

во согласност со Регулативата (EC) No. 1272/2008
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oyj.
Safety data sheetTEMADUR 20 [GB-ENG]
Thinner safety data sheetTHINNER 1048 [GB-ENG]
Hardener safety data sheetHARDENER 008 7590 [GB-ENG]