Temathane 90

Tikkurila Industry 9L
ОПИС A two component, glossy polyurethane paint, hardener aliphatic isocyanate.
КАРАКТЕРИСТИКИ НА ПРОИЗВООДОТ Recommended to be used as a glossy topcoat for epoxy and polyurethane systems exposed to weathering.
Перпорачана употреба Recommended for painting of outside of storage tanks, steel buildings and other steelwork.

Features Excellent weathering and abrasion resistance.
A durable, easy to clean and non-chalking topcoat with good gloss and colour retention.
Gloss groups Gloss

Recommended film thicknesses

Theoretical coverage




40 µm

75 µm

13.7 m2/l


Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Разредувач 1048, 1067 and 1061
Mixing ratio Base 9 parts by volume 516-series
Hardener 1 part by volume 008 7620
Метод на примена By airless or conventional spray or by brush.
Pot-life (+23°C) 4 hours.
Drying times

DFT 40 µm

+ 5 ºC

+ 10 ºC

+ 23 ºC

+ 35 ºC

Dust dry, after

45 min

30 min

20 min

10 min

Touch dry, after

12 h

8 h

4 h

2½ h

Recoatable, after

No limitations.


Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Густина 1.2 ± 0.1 kg / l (mixed)
Шифра на производот 516-series

Услови за примена All surfaces must be dry. The temperature of the ambient air, surface or paint should not fall below +5ºC during application or drying. Relative humidity should not exceed 80%. The surface temperature of the steel should remain at least 3ºC above the dew point.
Припрема Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
Priming Temacoat GPL-S Primer, Temacoat GPL-S MIO, Temacoat RM 40, Temacoat SPA, Temabond and Temadur 20.
Finishing Temadur and Temathane.
Премачкување By airless or conventional spray or by brush. In order to obtain an even, non-porous finish, spray a misty coat: first a thin layer, then let the solvents evaporate for
5 - 30 minutes and then apply the full coat. Depending on the application method and the temperature of the components (base, hardener, thinner) the paint can be thinned 25 - 35 %. The viscosity should be 20 - 25 s DIN4. Airless spray nozzle tip 0.011" - 0.013" and nozzle pressure 120 - 160 bar. Spray angle shall be chosen according to the shape of the object.
At conventional spray the viscosity should be 20 - 25 s DIN4.
At brush application the paint should be thinned according to the circumstancies.
Mixing of components First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use Temaspeed Squirrel Mixer for mixing.
Чистење на алатот Thinner 1048, 1067 or 1061.
EU VOC 2004/42/EC ограничена вредност The Volatile Organic Compounds amount is 425 g/litre of paint mixture.
VOC content of the paint mixture (thinned 35 % by volume) is 550 g/litre.

во согласност со Регулативата (EC) No. 1272/2008
For industrial use only. Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oyj.
Safety data sheetTEMATHANE 90 [GB-ENG]
Thinner safety data sheetTHINNER 1048 [GB-ENG]
Hardener safety data sheetHARDENER 008 7620 [GB-ENG]